Porcelain repair - Influence of different systems and surface treatments on resin bond strength
- 주제(키워드) Composite resin , Porcelain repair , Shear bond strength , Tribochemical silica coating
- 등재 SCIE, KCI등재, SCOPUS
- 발행기관 Korean Academy of Prosthodontic
- 발행년도 2015
- 총서유형 Journal
- URI http://www.dcollection.net/handler/ewha/000000120470
- 본문언어 영어
- Published As http://dx.doi.org/10.4047/jap.2015.7.5.343
- 저작권 이화여자대학교 논문은 저작권에 의해 보호받습니다.
초록/요약
PURPOSE. The purpose of this study was to evaluate the bond strength of composite resin on the fracture surface of metal-ceramic depending on the repair systems and surface roughening methods. MATERIALS AND METHODS. A total of 30 disk specimens were fabricated, 15 of each were made from feldspathic porcelain and nickel-chromium base metal alloy. Each substrate was divided into three groups according to the repair method: a) application of repair system I (Intraoral Repair Kit) with diamond bur roughening (Group DP and DM), b) application of repair system I with airborne-particle abrasion (Group SP and SM), and c) application of repair system II (CoJet Intraoral Repair System, Group CP and CM). All specimens were thermocycled, and the shear bond strength was measured. The data were analyzed using the Kruskal-Wallis analysis and the Mann-Whitney test with a significance level of 0.05. RESULTS. For the porcelain specimens, group SP showed the highest shear bond strength (25.85 ± 3.51 MPa) and group DP and CP were not significantly different. In metal specimens, group CM showed superior values of bond strength (13.81 ± 3.45 MPa) compared to groups DM or SM. CONCLUSION. Airborne-particle abrasion and application of repair system I can be recommended in the case of a fracture localized to the porcelain. If the fracture extends to metal surface, the repair system II is worthy of consideration.
more