Quasi-ductile to brittle transitional behavior and material properties gradient for additively manufactured SLA acrylate
- 주제(키워드) Acrylate polymer , Additive manufacturing , Material properties gradient , SEM fractographic analysis , Strain rate dependency
- 관리정보기술 faculty
- 등재 SCIE, SCOPUS
- OA유형 Bronze
- 발행기관 Elsevier B.V.
- 발행년도 2022
- URI http://www.dcollection.net/handler/ewha/000000203201
- 본문언어 영어
- Published As https://doi.org/10.1016/j.matlet.2022.133121
초록/요약
This research investigates the correlation between post-curing conditions, thickness, stress–strain, and fracture behaviors of additively manufactured SLA acrylate polymer, utilizing tensile tests and scanning electron microscopic fractography analysis. Due to poor polymerization, low curing energy resulted in a quasi-ductile behavior and low strain rate sensitivity. In contrast, high energy promotes the redistribution of the fracture energy from failure strain to failure stress, leading to increased sensitivity. Furthermore, poorly cured specimens show clean fracture surfaces, contrasting with their quasi-ductile behavior, whereas highly cured specimens present rough surfaces, generally associated with ductile fracture. Therefore, increasing curing energy promotes a transition from a quasi-ductile to an almost perfectly brittle behavior and influences the material's elastic, plastic, and fracture behaviors, which appear to be non-uniform throughout the thickness, especially for thicker structures. © 2022 Elsevier B.V.
more